Al BasirAbu Bakar SulongNashrah Hani JamadonNorhamidi Muhamad2024-04-152024-04-152022Basir, A., Sulong, A.B., Jamadon, N.H. & Muhamad, N. (2022). Sintering behavior of bi-material micro-component of 17-4PH stainless steel and yttria-stabilized zirconia produced by two-component micro-powder injection molding process, Materials, 15(6), 2059.https://openscience.ukm.my/handle/123456789/73The tensile data of the two-component micro-specimens fabricated using stainless steel 17-4PH and Zirconia materials on the grounds of two-component micro-powder injection molding process were obtained following MPIF standard 10 using a universal testing machine (model 5566, INSTRON, Norwood, MA, USA) at a 0.1 mm/min rate with a 1 KN load cell. These data were required to understand the bonding strength of the fabricated samples.Two-component micro-powder injection molding17-4PH/zirconia micro-sized componentsSinteringMechanical propertiesTensile test data of sintered bi-material components processed via two-component micro-powder injection molding process